- 拉伸强度 [MPa]: 16.6
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 16.6 MPa | 2410 psi | |
| Elongation at Yield | 535 % | 535 % | |
| 100% Modulus | 0.00145 GPa | 0.210 ksi | |
| 200% Modulus | 0.00183 GPa | 0.265 ksi | |
| 300% Modulus | 0.00272 GPa | 0.395 ksi | |
| Tear Strength | 25.7 kN/m | 147 pli | Die C |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Cure Time | 7.00 min @Temperature 149 °C | 0.117 hour @Temperature 300 °F | |