- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1078 % | 1078 % | ASTM D882 |
| Film Elongation at Break, TD | 1368 % | 1368 % | ASTM D882 |
| Secant Modulus, MD | 0.214 GPa | 31.0 ksi | 1%; ASTM D882 |
| Secant Modulus, TD | 0.231 GPa | 33.5 ksi | 1%; ASTM D882 |
| Coefficient of Friction | 0.92 | 0.92 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 7.70 g/micron | 196 g/mil | ASTM 1922 |
| Elmendorf Tear Strength, TD | 17.8 g/micron | 452 g/mil | ASTM 1922 |
| Dart Drop | 2.65 g/micron | 67.3 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 44.0 MPa | 6380 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 57 % | 57 % | ASTM D1003 |
| Gloss | 3.0 % | 3.0 % | 60° angle; ASTM D2457 |