- 熔体流动速率 [g/10min]: 0.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.920 g/cc | 0.920 g/cc | ASTM D1505/D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 950 % | 950 % | ASTM D882 |
| Film Elongation at Break, TD | 1180 % | 1180 % | ASTM D882 |
| Elmendorf Tear Strength MD | 270 g | 270 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | gF; ASTM D1922 |
| Dart drop Test | 170 g | 0.375 lb | gF/50%f; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 170 MPa | 24700 psi | ASTM D882 |
| 1% Secant Modulus, TD | 180 MPa | 26100 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 35 % @Thickness 0.0250 mm | 35 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 49 % @Thickness 0.0250 mm | 49 % @Thickness 0.000984 in | 60°; ASTM D2457 |