- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM-D792 |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 990 % | 990 % | ASTM-D882 |
| Film Elongation at Break, TD | 1440 % | 1440 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 180 g | 180 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 0.530 g/micron | 13.5 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 4.74 g/micron | 120 g/mil | ASTM-D1922 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 320 MPa | 46400 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 380 MPa | 55100 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 44 % | 44 % | ASTM-D1003 |
| Gloss | 45 % | 45 % | Angle 60°; ASTM-D2457 |