- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238E | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 580 % | 580 % | ASTM D882 | ||
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 | ||
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 11.8 g/micron | 300 g/mil | Notched; ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 21.7 g/micron | 550 g/mil | Notched; ASTM D1992 | ||
| Dart Drop | 4.41 g/micron | 112 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 42.7 MPa | 6200 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 33.1 MPa | 4800 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 214 MPa | 31000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D1003 | ||
| Gloss | 84 % | 84 % | 45°; ASTM D2457 | ||
| 140 % | 140 % | 60°; ASTM D2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 270 °C | 518 °F | Cast Film | ||
| Die Opening | 0.0640 cm | 0.0252 in | |||
| Extruder Size | 6.35 cm | 2.50 in | |||
| Descriptive Properties | |||||
| Color | Natural | ||||