- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882 |
| Secant Modulus, MD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 17.7 g/micron | 450 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 28.3 g/micron | 720 g/mil | ASTM D1922 |
| Dart Drop | 3.80 g/micron | 96.5 g/mil | F50; 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 46.0 MPa | 6670 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.0 MPa | 6670 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.5 % | 3.5 % | ASTM D2457 |
| Gloss | 136 % | 136 % | at 60°. ASTM D 2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 °C | 518 °F | |