- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 24.1 MPa @Thickness 0.0200 mm | 3500 psi @Thickness 0.000787 in | Transverse to Flow; ASTM D882 |
| 29.6 MPa @Thickness 0.0200 mm | 4290 psi @Thickness 0.000787 in | Direction of Flow; ASTM D882 | |
| Elongation at Break | 750 % @Thickness 0.0200 mm | 750 % @Thickness 0.000787 in | Transverse to Flow; ASTM D882 |
| 800 % @Thickness 0.0200 mm | 800 % @Thickness 0.000787 in | Direction of Flow; ASTM D882 | |
| Dart Drop, Total Energy | 130 J | 95.9 ft-lb | F50; ASTM D1709 |
| Tear Strength Test | 350 @Thickness 0.0200 mm | 350 @Thickness 0.000787 in | g; Direction of Flow; ASTM D1922 |
| 350 @Thickness 0.0200 mm | 350 @Thickness 0.000787 in | g; Transverse to Flow; ASTM D1922 | |