- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D4883 |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | 2.0 | 2.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 18.5 g/micron | 470 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.8 g/micron | 630 g/mil | ASTM D1922 |
| Dart Drop | 42.5 g/micron | 1080 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 1350 g | 2.98 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 62.8 MPa | 9110 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 49.0 MPa | 7110 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.3 % | 5.3 % | ASTM D2457 |
| Gloss | 82 % | 82 % | 60°; ASTM D 2457 |
| 130 % | 130 % | 45°; ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 °C | 450 °F | |