- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.791 MPa | 1275 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.163 MPa | 1184 psi | ASTM D882 |
| Film Elongation at Break, MD | 462 % | 462 % | ASTM D882 |
| Film Elongation at Break, TD | 649 % | 649 % | ASTM D882 |
| Impact | 267 | 267 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 2061 | 2061 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| 2125 | 2125 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| Elmendorf Tear Strength MD | 338 g | 338 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 507 g | 507 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 16.63 g/micron | 422.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.951 g/micron | 633.75 g/mil | ASTM D1922 |
| Dart drop Test | 208 g | 0.459 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.10 MPa | 7267 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.79 MPa | 4176 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.40 % | 0.40 % | ASTM D1003 |
| Gloss | 95 % | 95 % | 45°; ASTM D2457 |