- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.3 MPa | 1780 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.5 MPa | 1520 psi | ASTM D882 |
| Film Elongation at Break, MD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Secant Modulus, MD | 0.292 GPa | 42.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.332 GPa | 48.2 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 140 g | 140 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 460 g | 460 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.61 g/micron | 117 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 15.1 g/micron | 383 g/mil | ASTM D1922 |
| Dart Drop | 3.11 g/micron | 79.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 95.0 g | 0.209 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 46.0 MPa | 6670 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 38.0 MPa | 5510 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 24 % | 24 % | ASTM D1003 |
| Gloss | 39 % | 39 % | 45°, ASTM D-2457 |