- 熔体流动速率 [g/10min]: 2.35
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 2.35 g/10 min | 2.35 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.40 MPa | 1070 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.60 MPa | 1100 psi | ASTM D882 |
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D882 |
| Secant Modulus, MD | 0.126 GPa | 18.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.159 GPa | 23.1 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 840 g | 840 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 9.84 g/micron | 250 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 41.3 g/micron | 1050 g/mil | ASTM D1922 |
| Dart Drop | 4.17 g/micron | 106 g/mil | F50; ASTM D1709 |
| Dart drop Test | 85.0 g | 0.187 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 66.7 MPa | 9670 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Gloss | 92 % | 92 % | 45°, ASTM D-2457 |