- 熔体流动速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 190 °C | 22 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 49 | 49 | ISO 868 |
| Elongation at Break | 130 % | 130 % | At 5 mm/min; ISO 527-2 |
| Tensile Modulus | 0.180 GPa | 26.1 ksi | At 1 mm/min; ISO 527-2 |
| Tensile Impact Strength | 160 kJ/m² | 76.1 ft-lb/in² | ISO 8256/A1 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 °C | 198 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 180 - 230 °C | 356 - 446 °F | |
| Mold Temperature | 10.0 - 40.0 °C | 50.0 - 104 °F | |