- 密度 [g/cm3]: 0.915
- 拉伸强度 [MPa]: 9.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.915 - 0.919 g/cc | 0.0331 - 0.0332 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 25 - 35 g/10 min @Load 2.16 kg, Temperature 190 °C | 25 - 35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 7.00 MPa | 1020 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 108 °C | 226 °F | ASTM D3418 |
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 170 - 210 °C | 338 - 410 °F | |
| Die Cooling Temperature | 25.0 - 45.0 °C | 77.0 - 113 °F | |