- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 4.6 % | 4.6 % | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 24.7 MPa | 3580 psi | Transverse to Flow; ASTM D882 |
| 25.9 MPa | 3760 psi | Direction of Flow; ASTM D882 | |
| Elongation at Break | 180 % | 180 % | Direction of Flow; ASTM D882 |
| 580 % | 580 % | Transverse to Flow; ASTM D882 | |
| 1% Secant Modulus | 146 MPa | 21200 psi | Direction of Flow; ASTM D882 |
| 168 MPa | 24400 psi | Transverse to Flow; ASTM D882 | |
| Dart Drop, Total Energy | 190 J | 140 ft-lb | F50; ASTM D1790 |
| Tear Strength Test | 90 | 90 | g; Transverse to Flow; ASTM D1922 |
| 200 | 200 | g; Direction of Flow; ASTM D1922 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 89.0 °C | 192 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.4 % | 6.4 % | ASTM D1003 |
| Gloss | 71 % | 71 % | 45°; ASTM D2457 |