- 熔体流动速率 [g/10min]: 0.88
- 密度 [g/cm3]: 0.9239
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9239 g/cc | 0.03338 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.88 g/10 min | 0.88 g/10 min | ASTM D1238 |
| Antiblock Level | 1245 ppm | 1245 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.8 MPa | 1710 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.22 MPa | 1773 psi | ASTM D882 |
| Film Elongation at Break, MD | 370 % | 370 % | ASTM D882 |
| Film Elongation at Break, TD | 557 % | 557 % | ASTM D882 |
| Secant Modulus, MD | 0.201099 GPa | 29.1675 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.22661 GPa | 32.868 ksi | 2% Secant; ASTM D882 |
| Impact | 780 | 780 | [ft-lbf/in3]; Toughness MD; ASTM D882 |
| 808 | 808 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 400 g | 400 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 449 g | 449 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.87 g/micron | 200 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.839 g/micron | 224.5 g/mil | ASTM D1922 |
| Dart drop Test | 115 g | 0.254 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.56 MPa | 3127 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.87 MPa | 2447 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 234 °F | Dow Method (DSC) |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 76 % | 76 % | 45°; ASTM D2457 |