- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 9.6
- 弯曲强度 [MPa]: 18.6
- 弯曲模量 [MPa]: 0.238
- 热变形温度 [℃]: 44.0
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | ASTM D2240 |
| Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
| Tensile Strength, Yield | 9.60 MPa | 1390 psi | ASTM D638 |
| Elongation at Break | 620 % | 620 % | ASTM D638 |
| Modulus of Elasticity | 0.186 GPa | 27.0 ksi | ASTM D638 |
| Flexural Modulus | 0.238 GPa | 34.5 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| 0.430 J/cm @Temperature -40.0 °C | 0.806 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 93.0 °C | 199 °F | Freezing Point via DSC/ASTM D3418 |
| 109 °C | 228 °F | Upon Melting via DSC/ASTM D3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.51 | 1.51 | ASTM D542 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 193 °C | 379 °F | Typical die temp for tube extrusion. |
| Melt Temperature | 188 °C | 370 °F | tube extrusion |