- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.927
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 5.0 % | 5.0 % | |||
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 320 % | 320 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 180 g | 180 g | ASTM D1922 | ||
| Dart drop Test | 140 g | 0.309 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.8 MPa | 3600 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 19.3 MPa | 2800 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 131 MPa | 19000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 165 MPa | 24000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM D1003 | ||
| Gloss | 75 % | 75 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 191 °C | 375 °F | |||
| Descriptive Properties | |||||
| Antiblock | Low | ||||
| Slip | Medium | ||||