- 密度 [g/cm3]: 0.957
- 缺口冲击强度: 4.27
- 弯曲强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 0.862
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.957 g/cc | 0.0346 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature >=50.0 °C | >= 1000 hour @Temperature >=122 °F | Igepal (no failures); ASTM F1248 |
| ESCR 100% Igepal® | >= 5000 hour | >= 5000 hour | no failures; ASTM D 1693C |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 49 | 49 | ASTM D785 |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Ultimate | >= 22.8 MPa @Thickness 3.17 mm | >= 3300 psi @Thickness 0.125 in | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.862 GPa | 125 ksi | at 2% Strain; ASTM D3350 |
| 2% Secant Modulus | 0.793 GPa | 115 ksi | ASTM D638 |
| Izod Impact, Notched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D 256A |
| Hydrostatic Design Basis | 11.0 MPa | 1600 psi | 100,000 hrs.; ASTM D2837 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 µm/m-°C @Temperature 20.0 °C | 100 µin/in-°F @Temperature 68.0 °F | ASTM D648 |
| Melting Point | 127 °C | 260 °F | ASTM D3417 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | -118 °C | -180 °F | ASTM D746 |