- 密度 [g/cm3]: 2.15
- 弯曲强度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.15 g/cc | 0.0777 lb/in³ | Sintered moldings; ASTM D4894/D4895 |
| Apparent Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | DIN 53 466 |
| Linear Mold Shrinkage | 0.027 cm/cm @Thickness 80.0 mm | 0.027 in/in @Thickness 3.15 in | sheet; ASTM D4894 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.0 MPa @Thickness 2.00 mm | 2470 psi @Thickness 0.0787 in | ASTM D4894 |
| Elongation at Break | 250 % @Thickness 2.00 mm | 250 % @Thickness 0.0787 in | ASTM D4894 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature 30.0 - 100 °C | 61.1 µin/in-°F @Temperature 86.0 - 212 °F | |
| 120 µm/m-°C @Temperature 30.0 - 200 °C | 66.7 µin/in-°F @Temperature 86.0 - 392 °F | ||
| 140 µm/m-°C @Temperature 30.0 - 300 °C | 77.8 µin/in-°F @Temperature 86.0 - 572 °F | ||
| Thermal Conductivity | 0.800 W/m-K | 5.55 BTU-in/hr-ft²-°F | DIN 52 612 |