- 密度 [g/cm3]: 2.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | DIN EN ISO 60 | ||
| Density | 2.15 g/cc | 0.0777 lb/in³ | Sintered Sheets; DIN EN ISO 12086 | ||
| Particle Size | 550 µm | 550 µm | average; ISO 13320 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 34.0 MPa | 4930 psi | Sintered Sheet; DIN EN ISO 527-3 | ||
| Elongation at Break | 400 % | 400 % | DIN EN ISO 527-3 | ||
| Descriptive Properties | |||||
| Extrusion Pressure | 26 MPa | reduction ratio 400, ASTM D4895 | |||
| Reduction Ratio Range | 20-1000:1 | Dyneon Method | |||