- 熔体流动速率 [g/10min]: 9.5
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 2.3
- 弯曲强度 [MPa]: 67.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | |
| Water Absorption | 2.3 % | 2.3 % | |
| Moisture Absorption at Equilibrium | 1.05 % | 1.05 % | Humidity Absorption |
| Melt Flow | 9.5 g/10 min @Load 2.16 kg, Temperature 275 °C | 9.5 g/10 min @Load 4.76 lb, Temperature 527 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5 mm/min |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min |
| Tensile Modulus | 5.50 GPa | 798 ksi | 1 mm/min |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | |
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||