- 熔体流动速率 [g/10min]: 80.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 7.0
- 弯曲强度 [MPa]: 60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 148 cm³/g | 148 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM Data; MD | ||
| Melt Flow | 80 g/10 min @Load 5.00 kg, Temperature 275 °C | 80 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 12 % | 12 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 9.20 J/cm² | 43.8 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.5 @Frequency 1.00e+6 Hz | 5.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.16 @Frequency 1.00e+6 Hz | 0.16 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10 K/min | ||
| 260 °C | 500 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||