- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 5.7
- 缺口冲击强度: 12.0
- 弯曲强度 [MPa]: 195.0
- 弯曲模量 [MPa]: 9.60
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.7 % | 5.7 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 23°C/50% R.H.; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 195 MPa | 28300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 9.60 GPa | 1390 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | 10 K/min | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||