- 密度 [g/cm3]: 1.36
- 断裂伸长率 [%]: 140
- 弯曲强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 4.48
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM data at 5 mm/min. |
| 86.0 MPa | 12500 psi | ISO value at 5mm/min. | |
| Elongation at Break | 8.0 % | 8.0 % | Strain at break, ISO, 5 mm/min |
| 8.0 % | 8.0 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 140 MPa | 20300 psi | ASTM Data |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |