热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
图
| 参数： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 g/cc @Temperature 23.0 °C |
1.20 g/cc @Temperature 73.4 °F |
ASTM D792 | ||
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0070 in/in @Temperature 73.4 °F |
ASTM D955 | ||
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C |
21 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM D785 | ||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 60 % | 60 % | 50mm/min; ASTM D638 | ||
| Flexural Strength | 90.0 MPa | 13100 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.20 mm, Temperature -10.0 °C |
5.99 ft-lb/in @Thickness 0.126 in, Temperature 14.0 °F |
ASTM D256 | ||
| 5.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
9.55 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 | ||
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | 1.6mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|||
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 275 °C | <= 527 °F | |||
| Rear Barrel Temperature | 230 - 255 °C | 446 - 491 °F | Start Point: 235°C | ||
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Start Point: 245°C | ||
| Front Barrel Temperature | 235 - 270 °C | 455 - 518 °F | Start Point: 255°C | ||
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Start Point: 240°C | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C | ||
| Drying Temperature | 80.0 - 90.0 °C @Time 7200 - 14400 sec |
176 - 194 °F @Time 2.00 - 4.00 hour |
Pre-dry | ||
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |||
| De |
|||||
| Injection Speed | 30-80% | ||||
特征：
无卤阻燃V-0 / 1.5mm，
出色的平衡性能
高耐热性
良好的耐化学性
良好的耐水解性
适用于涂料和电镀
下拉电阻
应用：
液晶电视，显示器，PDP
激光打印机，复印机
笔记本电脑和充电器
可充电电池
汽车dvd
电动工具充电器
电信设备
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com