类别： |
酯，热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）；冲击改性聚碳酸 |
| 材料说明： | 描述：注塑，PC / ABS，高流动性，高冲击 |
| 应用： | l.E和E（房屋） |
  |
|
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
5.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 100 % @Thickness 3.20 mm |
>= 100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 86.3 MPa @Thickness 3.20 mm |
12500 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm |
327 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.41 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
>= 8.27 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| >= 6.18 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 11.6 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness >=1.60 mm |
140 °F @Thickness >=0.0630 in |
|
| 60.0 °C @Thickness >=3.00 mm |
140 °F @Thickness >=0.118 in |
||
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness >=1.60 mm |
140 °F @Thickness >=0.0630 in |
|
| 60.0 °C @Thickness >=3.00 mm |
140 °F @Thickness >=0.118 in |
||
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness >=1.60 mm |
140 °F @Thickness >=0.0630 in |
|
| 60.0 °C @Thickness >=3.00 mm |
140 °F @Thickness >=0.118 in |
||
| Flammability, UL94 | HB @Thickness >=1.60 mm |
HB @Thickness >=0.0630 in |
|
| HB @Thickness >=3.00 mm |
HB @Thickness >=0.118 in |
||
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Front Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Nozzle Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |