TPU 95 P 5044 物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D995 | ||
| Melt Flow | 40 - 70 g/10 min | 40 - 70 g/10 min | Melt Volume Rate (cm³/10 min) | ||
| Melt Index of Compound | 55 g/10 min @Load 21.6 kg, Temperature 190 °C |
55 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm3/10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 92 | 92 | ASTM D2240 | ||
| Hardness, Shore D | 39 | 39 | ASTM D2240 | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | DIN 53504 | ||
| Elongation at Break | 670 % | 670 % | ASTM D412 | ||
| 100% Modulus | 0.00910 GPa | 1.32 ksi | DIN 53504 | ||
| 300% Modulus | 0.0159 GPa | 2.31 ksi | DIN 53504 | ||
| Rebound | 34 % | 34 % | Bayshore; ASTM D2632 | ||
| Tear Strength | 116 kN/m | 660 pli | ASTM D624 | ||
| Abrasion | 30 | 30 | [mm3]; ISO 4649 | ||
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec |
25 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 | ||
| 41 % @Temperature 70.0 °C, Time 86400 sec |
41 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 160 - 170 °C | 320 - 338 °F | Huntsman/TMA | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | ||
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion | ||
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion | ||
| 180 - 200 °C | 356 - 392 °F | Injection | |||
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion | ||
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion | ||
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection | ||
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection | ||
| De |
|||||
| Heating Zone | 175-195°C |
||||
应用领域：
1.鞋类：运动鞋Logo、运动鞋气垫、登山鞋、雪鞋、高尔夫球鞋、溜冰鞋、之面料及内里贴合材料。
2.成衣类：雪衣、雨衣、风衣、防寒夹克、野战服、纸尿裤、 生理裤、等面料复合材料(防水透湿)。
3医药类：手术衣、帽、鞋、 医院用褥垫、冰袋、绷带、血浆袋、外科用包扎布条、口罩、等面料及内里材料，手术床气囊。
4国防用品：飞机油箱，武器封存覆膜、帐棚窗口、军用水袋、救生衣，充汽艇等之面料及内里面料，气囊。
5.运动用品：足球表面及内胆、充气床、饮水袋、滑雪手套(防水袋)、潜水衣、雪衣、泳装、滑雪板、商标、气囊、运动衫、瘦身衣等面料及内里材料。
优良的抗微生物性，高低温适应性，特别适用于电缆护套及软管类产品。
上海松翰塑化科技有限公司长期供应原料产品，品质一流，TPU/TPV种类齐全。 咨询人褚先生 电话13721478039 QQ297262310 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询