Availability
|
|
|
Forms
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.14
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow
|
1.8
|
%
|
ASTM D955 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
121
|
|
ASTM D785 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
3000
|
MPa
|
ASTM D638 |
|
Tensile Strength
|
ASTM D638 | ||
|
Yield
|
82.0
|
MPa
|
|
|
Break
|
50.0
|
MPa
|
|
|
Tensile Elongation
|
ASTM D638 | ||
|
Yield
|
5.0
|
%
|
|
|
Break
|
100
|
%
|
|
|
Flexural Modulus
|
3000
|
MPa
|
ASTM D790 |
|
Flexural Strength
|
113
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact
|
38
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
ASTM D648 | ||
|
0.45 MPa, Unannealed
|
180
|
°C
|
|
|
1.8 MPa, Unannealed
|
65.0
|
°C
|
|
|
Melting Temperature
|
265
|
°C
|