德国拜耳 PC Apec®1797 物性表

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³	ISO 1183-1
Moisture Absorption at Equilibrium	0.12 %	0.12 %	ISO 62, 50% RH
Water Absorption at Saturation	0.30 %	0.30 %	ISO 62
Melt Flow	31 g/10 min @Load 2.16 kg, Temperature 330 °C	31 g/10 min @Load 4.76 lb, Temperature 626 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	71.0 MPa	10300 psi	50 mm/min; ISO 527-1,-2
Elongation at Break	>= 50 %	>= 50 %	Nominal, 50 mm/min; ISO 527-1,-2
Elongation at Yield	6.6 %	6.6 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	2.40 GPa	348 ksi	1 mm/min; ISO 527-1,-2
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179-1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179-1eU
Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+17 ohm-cm	1.00e+17 ohm-cm	IEC 60093
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	IEC 60093
Dielectric Constant	2.9 @Frequency 1.00e+6 Hz	2.9 @Frequency 1.00e+6 Hz	IEC 60250
	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz	IEC 60250
Dielectric Strength	35.0 kV/mm @Thickness 1.00 mm	889 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz	IEC 60250
	0.0090 @Frequency 1.00e+6 Hz	0.0090 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	125 V	125 V	CTI M; Solution B; IEC 60112
	250 V	250 V	Solution A; IEC 60112
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	65.0 µm/m-°C @Temperature 23.0 - 55.0 °C	36.1 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1,-2
CTE, linear, Transverse to Flow	65.0 µm/m-°C @Temperature 23.0 - 55.0 °C	36.1 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1,-2
Maximum Service Temperature, Air	200 °C	392 °F
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F	ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)	147 °C	297 °F	ISO 75-1,-2
Vicat Softening Point	172 °C @Load 5.10 kg	342 °F @Load 11.2 lb	120°C/h; ISO 306
Minimum Service Temperature, Air	-30.0 °C	-22.0 °F
UL RTI, Electrical	140 °C	284 °F	UL 746B
UL RTI, Mechanical with Impact	130 °C	266 °F	UL 746B
UL RTI, Mechanical without Impact	140 °C	284 °F	UL 746B
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in
Optical Properties	Metric	English	Comments
Refractive Index	1.576	1.576	Procedure A; ISO 489
Transmission, Visible	89 % @Thickness 1.00 mm	89 % @Thickness 0.0394 in	ISO 13468-2
Processing Properties	Metric	English	Comments
Melt Temperature	330 °C	626 °F	Injection molding; ISO 294
Mold Temperature	100 °C	212 °F	Injection molding; ISO 294
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294
Descriptive Properties
Electrolytic Corrosion	A1	IEC 60426

生产厂家：德国拜耳
生产型号： PC Apec®1797
德国拜耳分类：聚合物;热塑性;聚碳酸酯（PC）;聚碳酸酯，高耐热;聚碳酸酯成型;聚碳酸酯，紫外线稳定

德国拜耳 PC Apec®1797 原材料内颗粒图：


德国拜耳 PC Apec®1797 原材料成型图咧：

             德国拜耳 PC Apec®1797 聚碳酸酯 PC
PC 中文名 聚碳酸酯   俗称：防弹胶   五大工程塑胶中唯一的透明产品
PC特性： 透明、尺寸稳定、抗冲击性好、耐热、天然防火、V2级，聚碳酸酯耐弱酸，耐中性油
缺点：不耐紫外光，不耐候，不耐强碱，不易加工，易脆，不耐磨，不抗刮花
PC高温下水解
不耐磨一些用于易磨损用途的PC器件需要对其表面进行特殊处理
针对PC不抗刮花 美国GE生产出一款抗刮花DMX开头的PC
美国GE生产一款耐低温 以EXL开头PC
PC  相对密度1.19~1.2%   透光89% 热变型温度135度左右，长期使用温度-60~120度   
针对PC的缺点对其改性增强   PC密度在1.2%以上
1.》PC加工困难，易粘模，加脱模剂，使它不粘模 R，
2.》PC不耐候，不耐紫外，对其添加UV剂，抗紫外
3.》玻璃纤维增强GF，提高强度，耐热温度
4.》阻燃增强V    阻燃等级
5.》碳纤维增强   导电，电磁屏蔽（EMI)
6.》铁氟龙PTFE增强L，耐磨，耐化学性好
7.》与其它材料合金
          德国拜耳 PC Apec®1797 主要应用分类
导光PC   主要用作 LCD 出光 LC1500 价格39  LC1700  价格 43
 
光扩散 主要用作LED灯罩  扩散率80~85%  日本帝人ML-1103 价格 60
 
吹瓶      矿泉水瓶 德国拜耳1239 价格 28
 
光学    照相机、显微镜、望远镜的镜头，太阳眼镜镜片，汽车灯 透明度 90%以上  LG-DOW 1080-70       极低的粘度 良好的脱模性
 
光碟级    专做光盘 流动性溶指60以上 三菱H-4000 价格38 基础创新OQ1023 价格 23
 
遮光     主要用做LCD 日本出光 URX2501
PC合金  PC/ABS  PC/PBT  PC/PET
             德国拜耳 PC Apec®1797 性能：
绝缘性能：优良（潮湿、高温也能保持电性能稳定,是制造电子、电气零件的理想材料）；
机械性能：强度高、耐疲劳性、尺寸稳定、蠕变也小（高温条件下也极少有变化）；

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！可提供以下报告：COA（产地证明）SGS（检测报告） MSDS（成分报告） FDA（食品安全报告） UL黄卡(出口报告)正规17%的正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
固定电话：021-5113184
联系QQ：996152797
联系信箱：996152797@qq.com