物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | ASTM D638 |
| Elongation at Break | 48 % | 48 % | ASTM D638 |
| Flexural Yield Strength | 79.3 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm |
2.49 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | |
样图：
尼龙66盐的制备
由二元酸和二元胺制取尼龙时，需要严格控制原料配比为等摩尔比，才能得到分子量较高的聚合物，因此，在生产中必须先把己二酸和己二胺混合制成尼龙66盐。尼龙66盐的制备是分别把己二胺的乙醇溶液与己二酸的乙醇溶液在60℃以上的温度下搅拌混合，中和成盐后析出，经过滤、醇洗、干燥，最后配制成63%左右的水溶液，供缩聚使用。反应式如下：
缩聚
尼龙66盐的缩聚需在高温下进行，伴随着水的脱除，生成线型高分子量尼龙66。
生产工艺分间歇法和连续法两种。连续法适合大规模生产，世界上生产尼龙66主要采用连续法。间歇法仅在两种情况下采用：一是生产特殊或试验品级;二是在生产能力为4 500t A 以下的小装置中。