PA66 A3WG6 BK00564 30%玻璃性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

Physical Properties	Metric	English	Comments
物性表：
Density	1.36 g/cc	0.0491 lb/in³	ISO 1183
Water Absorption	5.2 - 5.8 %	5.2 - 5.8 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	1.5 - 1.9 %	1.5 - 1.9 %	23°C; 50% RH; ISO 62
Viscosity Measurement	145	145	ISO 307
Linear Mold Shrinkage	0.0055 cm/cm	0.0055 in/in	restricted
Melt Flow	54.4 g/10 min @Load 5.00 kg, Temperature 275 °C	54.4 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	130 MPa	18900 psi	50 mm/min; ISO 527-1/-2
Elongation at Yield	5.0 %	5.0 %	50mm/min; ISO 527-1/-2
Modulus of Elasticity	7.20 GPa	1040 ksi	ISO 527-1/-2
Flexural Strength	210 MPa	30500 psi	at max force; ISO 178
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Izod Impact, Notched (ISO)	15.5 kJ/m² @Temperature 23.0 °C	7.38 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	10.0 J/cm² @Temperature 23.0 °C	47.6 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	2.20 J/cm² @Temperature 23.0 °C	10.5 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	5300 MPa @Strain <=0.500 %	769000 psi @Strain <=0.500 %	ISO 899-1

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Constant	5.6 @Frequency 1.00 Hz	5.6 @Frequency 1.00 Hz	IEC 60250
Dissipation Factor	0.30 @Frequency 1.00e+6 Hz	0.30 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	450 V	450 V	Test solution A; IEC 60112

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.350 W/m-K	2.43 BTU-in/hr-ft²-°F	DIN 52612
Melting Point	260 °C	500 °F	DIN 53765
Maximum Service Temperature, Air	145 °C	293 °F	for 50% loss of tensile strength after 20000hr
	175 °C	347 °F	for 50% loss of tensile strength after 5000hr
	240 °C	464 °F

Processing Properties	Metric	English	Comments
Melt Temperature	280 - 300 °C	536 - 572 °F	Injection-molding/Extrusion
Mold Temperature	80.0 - 90.0 °C	176 - 194 °F	Injection-molding

Descriptive Properties
Color	BK 00564
Commercial Status	Europe

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。 ...kl颗粒