物性表:
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | ||
Water Absorption | 3.7 - 4.3 % | 3.7 - 4.3 % | Saturation; ISO 62 | ||
Moisture Absorption at Equilibrium | 0.70 - 1.1 % | 0.70 - 1.1 % | 23°C; 50% RH; ISO 62 | ||
Viscosity Measurement | 140 | 140 | ISO 307 | ||
Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted | ||
Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 275 °C |
40 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength, Yield | 180 MPa | 26100 psi | 50 mm/min; ISO 527-1/-2 | ||
Elongation at Yield | 2.0 % | 2.0 % | 50 mm/min; ISO 527-1/-2 | ||
Modulus of Elasticity | 16.0 GPa | 2320 ksi | ISO 527-1/-2 | ||
Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 | ||
Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | ||
Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
Dielectric Constant | 3.6 @Frequency 1.00 Hz |
3.6 @Frequency 1.00 Hz |
IEC 60250 | ||
Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
Hot Wire Ignition, HWI | 1.0 sec @Thickness >=0.800 mm |
1.0 sec @Thickness >=0.0315 in |
ASTM D3874-88 | ||
High Amp Arc Ignition, HAI | 1.0 arcs @Thickness >=0.800 mm |
1.0 arcs @Thickness >=0.0315 in |
UL 746C | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 15.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
8.33 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 | ||
CTE, linear, Transverse to Flow | 40.0 - 50.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
22.2 - 27.8 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 | ||
Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 | ||
Melting Point | 260 °C | 500 °F | DIN 53765 | ||
Maximum Service Temperature, Air | 125 °C | 257 °F | for 50% loss of tensile strength after 20000hr | ||
145 °C | 293 °F | for 50% loss of tensile strength after 5000hr | |||
220 °C | 428 °F | ||||
Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
Decomposition Temperature | >= 310 °C | >= 590 °F | |||
UL RTI, Electrical | 115 °C @Thickness 1.50 mm |
239 °F @Thickness 0.0591 in |
UL 746B | ||
Flammability, UL94 | V-2 @Thickness >=0.800 mm |
V-2 @Thickness >=0.0315 in |
|||
V-0 @Thickness >=1.50 mm |
V-0 @Thickness >=0.0591 in |
||||
Oxygen Index | 28 % | 28 % | Limiting; ISO 4589-2 | ||
Glow Wire Test | 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
IEC 60695-2-12 | ||
Processing Properties | Metric | English | Comments | ||
Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
Zone 1 | 295 °C | 563 °F | Feed Zone | ||
Zone 2 | 295 °C | 563 °F | Compression | ||
Zone 3 | 295 °C | 563 °F | Metering-zone | ||
Zone 4 | 295 °C | 563 °F | Nozzle | ||
Melt Temperature | 295 °C | 563 °F | Optimal | ||
290 - 300 °C | 554 - 572 °F | Injection-molding/Extrusion | |||
Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
85.0 °C | 185 °F | Optimal | |||
Drying Temperature | 80.0 °C | 176 °F | |||
Dry Time | 4 hour | 4 hour | |||
Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
<= 0.15 % | <= 0.15 % | ||||
De |
|||||
Color | BK 23187 | ||||
Commercial Status | Europe | ||||
Ignition Temperature | >350°C | ASTM D1929 | |||
Peripheral Screw Speed | < 0.3 m/s |
在产品设计时,一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性,经常加入各种各样的改性剂。玻璃就是最常见的添加剂,有时为了提高抗冲击性还加入合成橡胶,如EPDM和SBR等。PA66的粘性较低,因此流动性很好(但不如PA6)。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。