PA66 A3W2G10 BK20560 机械强度较高_产品资讯

PA66 A3W2G10 BK20560 材料的密度1.30-1.40g/cm^3 一、性能指标: 外观微黄色均匀颗粒相对密度 1.30～1.40 含湿量(%) ≤1.5 拉伸强度(MPa) ≥150 静弯曲强度(MPa) ≥220 弯曲弹性模量(MPa) ≥6.5×103 缺口冲击强度(KJ/m2) ≥15 热变形温度(1.81MPa，℃) ≥210 玻璃纤维含量(%) 30±2 二、用途本产品居于高强度、高耐热性、热胀系数和收缩率小，吸水性低，尺寸稳定性随大气湿度和温度变化而不大，它适合制作凸轮、伐座、收音机零部件、电子仪表零件、汽车交通零部件等。

Physical Properties	Metric	English	Comments
物性表：
Bulk Density	0.500 - 0.800 g/cc	0.0181 - 0.0289 lb/in³
Density	1.55 g/cc	0.0560 lb/in³	ISO 1183
Water Absorption	3.7 - 4.3 %	3.7 - 4.3 %	ISO 62
Moisture Absorption at Equilibrium	1.0 - 1.4 %	1.0 - 1.4 %	ISO 62
Viscosity Measurement	140	140	ISO 307
Linear Mold Shrinkage	0.0035 cm/cm	0.0035 in/in
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 2577
Linear Mold Shrinkage, Transverse	0.0085 cm/cm	0.0085 in/in	ISO 2577
Melt Flow	15.5 g/10 min @Load 5.00 kg, Temperature 275 °C	15.5 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	255 MPa	37000 psi	ISO 527-1/-2
Elongation at Break	2.8 %	2.8 %	ISO 527-1/-2
Modulus of Elasticity	16.0 GPa	2320 ksi	ISO 527-1/-2
Charpy Impact Unnotched	10.0 J/cm² @Temperature 23.0 °C	47.6 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	ISO 11357-1/-3
Maximum Service Temperature, Air	240 °C	464 °F
Deflection Temperature at 0.46 MPa (66 psi)	250 °C	482 °F	ISO 527-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	250 °C	482 °F	ISO 527-1/-2
Decomposition Temperature	>= 310 °C	>= 590 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Processing Properties	Metric	English	Comments
Processing Temperature	80.0 °C	176 °F	Hopper Throat
Zone 1	300 °C	572 °F	Feed zone
Zone 2	300 °C	572 °F	Compression
Zone 3	300 °C	572 °F	Metering-zone
Zone 4	300 °C	572 °F	Nozzle
Melt Temperature	280 - 310 °C	536 - 590 °F	Injection Molding/Extrusion
	300 °C	572 °F	Optimal
Mold Temperature	80.0 °C	176 °F	Optimal
	80.0 - 90.0 °C	176 - 194 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F
Dry Time	4 hour	4 hour
Moisture Content	0.030 - 0.060 %	0.030 - 0.060 %	Optimal
	<= 0.15 %	<= 0.15 %

Descriptive Properties
Color	BK 20560
Commercial Status	Europe
Ignition Temperature	>400°C	ASTM D1929
Peripheral Screw Speed	< 0.3 m/s

特性:

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

样图:

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。