PA66 G/25-V0KB1 NAT0046 具高抗张强度_产品资讯

PA66 G/25-V0KB1 NAT0046 熔化温度：260~290℃。对玻璃添加剂的产品为275~280℃。熔化温度应避免高于300℃。模具温度：建议80℃。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于薄壁塑件，如果使用低于40℃的模具温度，则塑件的结晶度将随着时间而变化，为了保持塑件的几何稳定性，需要进行退火处理。

Physical Properties	Metric	English	Comments
物性表：
Density	1.35 g/cc	0.0488 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	145 MPa	21000 psi	ISO 527
Elongation at Break	2.4 %	2.4 %	ISO 527
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
Izod Impact, Notched (ISO)	7.70 kJ/m²	3.66 ft-lb/in²	ISO 180
Charpy Impact, Notched	0.850 J/cm²	4.04 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	ISO 75

Processing Properties	Metric	English	Comments
Melt Temperature	285 - 300 °C	545 - 572 °F
Mold Temperature	80.0 - 90.0 °C	176 - 194 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.050 %	<= 0.050 %

Descriptive Properties
Color	NAT 0046
Commercial Status	North America

性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。