PA66 SGKGS6 PA66-GF30 FR

物性表：
Physical Properties	Metric	English	Comments
Density	1.44 g/cc	0.0520 lb/in³	dry; ISO 1183
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	Sim. To ISO 294-4
Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	150 MPa	21800 psi	dry; ISO 527-1/-2
Elongation at Break	2.8 %	2.8 %	dry; ISO 527-1/-2
Tensile Modulus	11.0 GPa	1600 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	6.30 J/cm² @Temperature 23.0 °C	30.0 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eU
Charpy Impact, Notched	0.900 J/cm² @Temperature 23.0 °C	4.28 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	dry; ISO 75-1/-2
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	dry; IEC 60695-11-10
	V-0 @Thickness 0.400 mm	V-0 @Thickness 0.0157 in	dry; IEC 60695-11-10

料的密度1.30-1.40g/cm^3   一、性能指标: 外观 微黄色均匀颗粒              相对密度 1.30～1.40              含湿量(%) ≤1.5               拉伸强度(MPa) ≥150              静弯曲强度(MPa) ≥220              弯曲弹性模量(MPa) ≥6.5×103               缺口冲击强度(KJ/m2) ≥15 热变形温度(1.81MPa，℃) ≥210              玻璃纤维含量(%) 30±2  二、用途         本产品居于高强度、高耐热性、热胀系数和收缩率小，吸水性低，尺寸稳定性随大气湿度和温度变化而不大，它适合制作凸轮、伐座、收音机零部件、电子仪表零件、汽车交通零部件等。