PA66 3010GN30 NAT PA66-GF30 耐韧

 PA66 3010GN30 NAT PA66-GF30   性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。

物性表：
Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	dry; ISO 1183
Moisture Absorption	1.60 %	1.60 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.012 cm/cm	0.012 in/in	ISO 294-4
Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
	170 MPa	24700 psi	dry; ISO 527-1/-2
Elongation at Break	2.0 %	2.0 %	dry; ISO 527-1/-2
	2.9 %	2.9 %	cond; ISO 527-1/-2
Tensile Modulus	8.00 GPa	1160 ksi	cond; ISO 527-1/-2
	11.5 GPa	1670 ksi	dry; ISO 527-1/-2
Flexural Strength	210 MPa	30500 psi	cond; ISO 178
	260 MPa	37700 psi	dry; ISO 178
Flexural Modulus	8.10 GPa	1170 ksi	cond; ISO 178
	10.4 GPa	1510 ksi	dry; ISO 178
Charpy Impact Unnotched	6.80 J/cm² @Temperature 23.0 °C	32.4 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eU
	7.00 J/cm² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eU
Charpy Impact, Notched	1.10 J/cm² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA
Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 3.00e+14 ohm-cm	>= 3.00e+14 ohm-cm	dry; IEC 60093
Surface Resistance	4.00e+14 ohm	4.00e+14 ohm	cond; IEC 60093
Dielectric Constant	4.0 @Frequency 100 Hz	4.0 @Frequency 100 Hz	dry; IEC 60250
	4.0 @Frequency 1.00e+6 Hz	4.0 @Frequency 1.00e+6 Hz	dry; IEC 60250
Dielectric Strength	23.0 kV/mm	584 kV/in	dry; IEC 60243-1
Dissipation Factor	0.0090 @Frequency 100 Hz	0.0090 @Frequency 100 Hz	dry; IEC 60250
	0.019 @Frequency 1.00e+6 Hz	0.019 @Frequency 1.00e+6 Hz	dry; IEC 60250
Comparative Tracking Index	175 V	175 V	dry; IEC 60112
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C	11.1 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	60.0 µm/m-°C	33.3 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	260 °C	500 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	243 °C	469 °F	dry; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	258 °C	496 °F	dry; ISO 75-1/-2
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	dry; IEC 60695-11-10

 连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。