| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 78 | 78 | ASTM D786 |
| Hardness, Rockwell R | 120 | 120 | ASTM D786 |
| Hardness, Shore D | 79 | 79 | |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Yield Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.550 J/cm | 1.03 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB @Thickness 3.20 mm |
NB @Thickness 0.126 in |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 190 sec | 190 sec | Tungsten electrode; ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。