PA66 LA30 材料说明：长纤维热塑性塑料：sepaz LFT产品，注射成型的长纤维增强热塑性塑料（LFT），使用的是独特的拉挤成型，彻底打湿的玻璃纤维提供了最佳的加固与传统的短玻璃纤维增强热塑性塑料塑性矩阵。成型部分由sepaz LFT中使用的几乎所有的消费品和工业制造行业，包括汽车，娱乐和体育，海洋，食品饮料。

Physical Properties	Metric	English	Comments

Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D792
Water Absorption	0.40 % @Time 86400 sec	0.40 % @Time 24.0 hour
Linear Mold Shrinkage	0.017 cm/cm	0.017 in/in
Linear Mold Shrinkage, Transverse	0.013 cm/cm	0.013 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	58.86 MPa	8537 psi	ASTM D638
Elongation at Break	50 %	50 %	ASTM D638
Flexural Strength	95.16 MPa	13800 psi	ASTM D790
Flexural Modulus	2.2563 GPa	327.25 ksi	ASTM D790
Izod Impact, Notched	1.77 J/cm	3.31 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	185 °C	365 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	145 °C	293 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 290 °C	500 - 554 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F

产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。