PA66 RF0077E 分类：聚合物;热塑性;尼龙;尼龙66;尼龙66，40％玻璃纤维填充

材质注：Starflam RF0077E是无卤无红磷的阻燃，玻璃纤维增强聚酰胺66注塑树脂（又称RF1007Z270）

Physical Properties	Metric	English	Comments
物性表：
Density	1.47 g/cc	0.0531 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 4.00 mm	0.0010 - 0.0030 in/in @Thickness 0.157 in	ISO 294
Linear Mold Shrinkage, Transverse	0.0070 - 0.011 cm/cm	0.0070 - 0.011 in/in	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
Elongation at Break	2.1 %	2.1 %	5 mm/min; ISO 527
Tensile Modulus	11.5 GPa	1670 ksi	1 mm/min; ISO 527
Flexural Strength	216 MPa	31300 psi	2 mm/min; ISO 178
Flexural Modulus	10.4 GPa	1510 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/m²	4.28 ft-lb/in²	80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO)	55.0 kJ/m²	26.2 ft-lb/in²	80x10x4; ISO 180/1U

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V @Thickness 3.00 mm	600 V @Thickness 0.118 in	IEC 60112
Hot Wire Ignition, HWI	>= 120 sec @Thickness 0.800 mm	>= 120 sec @Thickness 0.0315 in	PLC 0
	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	PLC 0
	>= 120 sec @Thickness 3.00 mm	>= 120 sec @Thickness 0.118 in	PLC 0
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 0.800 mm	>= 120 arcs @Thickness 0.0315 in	PLC 0
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	PLC 0
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	PLC 0

Thermal Properties	Metric	English	Comments
Hot Ball Pressure Test	240 °C @Thickness 3.00 mm	464 °F @Thickness 0.118 in	IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical	140 °C @Thickness 0.800 mm	284 °F @Thickness 0.0315 in
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in
UL RTI, Mechanical with Impact	110 °C @Thickness 0.800 mm	230 °F @Thickness 0.0315 in
	110 °C @Thickness 1.50 mm	230 °F @Thickness 0.0591 in
	110 °C @Thickness 3.00 mm	230 °F @Thickness 0.118 in
UL RTI, Mechanical without Impact	140 °C @Thickness 0.800 mm	284 °F @Thickness 0.0315 in
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	IEC 60695-11-10
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
Glow Wire Test	775 °C @Thickness 0.800 mm	1430 °F @Thickness 0.0315 in	Glow-Wire Ignition; IEC 60695-2-13
	775 °C @Thickness 1.50 mm	1430 °F @Thickness 0.0591 in	Glow-Wire Ignition; IEC 60695-2-13
	825 °C @Thickness 3.00 mm	1520 °F @Thickness 0.118 in	Glow-Wire Ignition; IEC 60695-2-13
	960 °C @Thickness 0.800 mm	1760 °F @Thickness 0.0315 in	Glow-Wire Flammability; IEC 60695-2-12
	960 °C @Thickness 1.50 mm	1760 °F @Thickness 0.0591 in	Glow-Wire Flammability; IEC 60695-2-12
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	Glow-Wire Flammability; IEC 60695-2-12

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 1
Middle Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 2
Front Barrel Temperature	270 - 280 °C	518 - 536 °F	Zone 3
Melt Temperature	270 - 280 °C	518 - 536 °F
Mold Temperature	60.0 - 100 °C	140 - 212 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.15 - 0.25 %	0.15 - 0.25 %

具有良好的耐磨性、耐热性、耐油性及耐化学药品性，还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及优异的机械强度。能满足静电消散和静电放电(ESD)防护的要求。