| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 1.10 % @Temperature 23.0 °C |
1.10 % @Temperature 73.4 °F |
50% RH; ISO 62 | ||
| Water Absorption at Saturation | 4.5 % @Temperature 23.0 °C |
4.5 % @Temperature 73.4 °F |
ISO 62-1 | ||
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in | on Tensile Bar; ISO 294 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell L | 114 | 114 | ISO 2039-2 | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | 5 mm/min; ISO 527 | ||
| Elongation at Break | 3.3 % | 3.3 % | 5 mm/min; ISO 527 | ||
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 280 MPa | 40600 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -40.0 °C |
4.28 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A | ||
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | |||
| 11.0 kJ/m² @Temperature -20.0 °C |
5.23 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |||
| 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | ||
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |||
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm |
483 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | ||
| Dissipation Factor | 0.0068 @Frequency 50.0 - 60.0 Hz |
0.0068 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 375 V | 375 V | M; IEC 60112 | ||
| 500 V | 500 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
12.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 78.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
43.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | ||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af | ||
| Vicat Softening Point | 255 °C | 491 °F | B/120; ISO 306 | ||
| 256 °C | 493 °F | B/50; ISO 306 | |||
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |||
| Flame Spread | 2.00 mm/min @Thickness 3.00 mm |
0.0787 in/min @Thickness 0.118 in |
FMVSS Buring Speed | ||
| 6.00 mm/min @Thickness 2.00 mm |
0.236 in/min @Thickness 0.0787 in |
FMVSS Buring Speed | |||
| Oxygen Index | 27 % | 27 % | ISO 4589 | ||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
Glow-Wire Flammability; IEC 60695-2-12 | ||
| 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
Glow-Wire Ignition; IEC 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Zone 1 | ||
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Zone 2 | ||
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Zone 3 | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | 0.20 % | 0.20 % | |||
| De |
|||||
| Potable Water | KTW | ||||
| UL f1 | f1 | ||||
PA66 AG7K 熔化温度：260~290℃。对玻璃添加剂的产品为275~280℃。PA66 AG7K 熔化温度应避免高于300℃。 PA66 AG7K 模具温度：建议80℃。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于薄壁塑件，如果使用低于40℃的模具温度，则塑件的结晶度将随着时间而变化，为了保持塑件的几何稳定性，需要进行退火处理。