颗粒：
| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0010 - 0.0040 in/in @Thickness 0.157 in |
E2P method |
| Ash | 33 % @Temperature 650 °C |
33 % @Temperature 1200 °F |
ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 6.10 GPa | 885 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A |
| 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 85.0 kJ/m² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | DSC; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % | |
干燥处理：如果加工前材料是密封的，那么就没有必要干燥。然而，如果储存容器被打开，那么建议在85℃的热空气中干燥处理。如果湿度大于0.2%，还需要进行105℃，12小时的真空干燥。