PA66 ALY430A 低温特性佳、_产品资讯

PA66 ALY430A 在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。 PA66的粘性较低，因此流动性很好（但不如PA6）。

Physical Properties	Metric	English	Comments
物性表：
Density	1.24 g/cc	0.0448 lb/in³	ISO 1183
Water Absorption at Saturation	5.0 % @Temperature 23.0 °C	5.0 % @Temperature 73.4 °F	ISO 62-1
Linear Mold Shrinkage, Flow	0.0010 - 0.0015 cm/cm	0.0010 - 0.0015 in/in	on Tensile Bar; E2P method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	190 MPa	27600 psi	5 mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	5 mm/min; ISO 527
Tensile Modulus	15.0 GPa	2180 ksi	1 mm/min; ISO 527
Flexural Strength	280 MPa	40600 psi	break, 2 mm/min; ISO 178
Flexural Modulus	12.5 GPa	1810 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature -40.0 °C	2.38 ft-lb/in² @Temperature -40.0 °F	80x10x4; ISO 180/1A
	6.00 kJ/m² @Temperature -20.0 °C	2.86 ft-lb/in² @Temperature -4.00 °F	80x10x4; ISO 180/1A
	8.00 kJ/m² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	80x10x4; ISO 180/1A

Electrical Properties	Metric	English	Comments
Volume Resistivity	178000 ohm-cm	178000 ohm-cm	IEC 60093
Surface Resistance	178000 ohm	178000 ohm	ROA; IEC 60093

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	17.0 µm/m-°C @Temperature 23.0 - 60.0 °C	9.44 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	105 µm/m-°C @Temperature 23.0 - 60.0 °C	58.3 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	255 °C	491 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	250 °C	482 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point	255 °C	491 °F	B/120; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
Oxygen Index	27 %	27 %	ISO 4589

Processing Properties	Metric	English	Comments
Zone 1	260 - 280 °C	500 - 536 °F
Zone 2	270 - 280 °C	518 - 536 °F
Zone 3	270 - 290 °C	518 - 554 °F
Melt Temperature	270 - 290 °C	518 - 554 °F
Mold Temperature	70.0 - 90.0 °C	158 - 194 °F
Drying Temperature	75.0 - 85.0 °C @Time 14400 - 21600 sec	167 - 185 °F @Time 4.00 - 6.00 hour
Moisture Content	0.20 %	0.20 %

这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。 PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。
H颗粒07

颗粒：

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。