PA66 15Y D52 冲击改性，注射成型、类别：聚合物；热塑性；尼龙；尼龙66；尼龙66，品位的影响材料说明：ast03是影响改性聚酰胺66树脂注塑成型。
颗粒图： B颗粒08

Physical Properties	Metric	English	Comments
物性表：
Density	1.10 g/cc	0.0397 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.015 - 0.020 cm/cm	0.015 - 0.020 in/in	on Tensile Bar; ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	65.0 MPa	9430 psi	50 mm/min; ISO 527
Elongation at Break	20 %	20 %	5 mm/min; ISO 527
Elongation at Yield	4.5 %	4.5 %	50 mm/min; ISO 527
Tensile Modulus	2.60 GPa	377 ksi	1 mm/min; ISO 527
Flexural Strength	90.0 MPa	13100 psi	yield, 2 mm/min; ISO 178
Flexural Modulus	2.40 GPa	348 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/m² @Temperature -40.0 °C	4.28 ft-lb/in² @Temperature -40.0 °F	Edgew 80x10x4 sp=62; ISO 180/1A
	11.0 kJ/m² @Temperature -20.0 °C	5.23 ft-lb/in² @Temperature -4.00 °F	Edgew 80x10x4 sp=62; ISO 180/1A
	12.0 kJ/m² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	Edgew 80x10x4 sp=62; ISO 180/1A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	60.0 µm/m-°C @Temperature 23.0 - 60.0 °C	33.3 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	92.0 µm/m-°C @Temperature 23.0 - 60.0 °C	51.1 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	200 °C	392 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	73.0 °C	163 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point	220 °C	428 °F	B/50; ISO 306
	225 °C	437 °F	B/120; ISO 306
UL RTI, Electrical	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
UL RTI, Mechanical with Impact	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
UL RTI, Mechanical without Impact	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	IEC 60695-11-10
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	IEC 60695-11-10

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	250 - 260 °C	482 - 500 °F	Zone 1
Middle Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 2
Front Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 3
Melt Temperature	265 - 275 °C	509 - 527 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
Drying Temperature	75.0 - 85.0 °C	167 - 185 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour
Moisture Content	0.20 %	0.20 %

PA66 聚酰胺66或尼龙66化学和物理特性PA66在聚酰胺材料中有较高的熔点。它是一种半晶体-晶体材料。PA66在较高温度也能保持较强的强度和刚度。在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。