| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.700 % @Temperature 23.0 °C |
0.700 % @Temperature 73.4 °F |
50% RH; ISO 62 | ||
| Water Absorption at Saturation | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
ISO 62-1 | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0025 cm/cm | 0.0010 - 0.0025 in/in | on Tensile Bar; ISO 294 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell L | 114 | 114 | ISO 2039-2 | ||
| Tensile Strength at Break | 200 MPa | 29000 psi | 5 mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 | ||
| Tensile Modulus | 14.5 GPa | 2100 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 310 MPa | 45000 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 13.5 GPa | 1960 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | ||
| 13.0 kJ/m² @Temperature -40.0 °C |
6.19 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A | |||
| 14.0 kJ/m² @Temperature -20.0 °C |
6.66 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |||
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |||
| Charpy Impact Unnotched | 14.0 J/cm² | 66.6 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |||
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm |
483 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | ||
| Dissipation Factor | 0.0068 @Frequency 50.0 - 60.0 Hz |
0.0068 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 350 V | 350 V | M; IEC 60112 | ||
| 500 V | 500 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
10.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 71.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
39.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | ||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af | ||
| Vicat Softening Point | 260 °C | 500 °F | B/120; ISO 306 | ||
| 260 °C | 500 °F | B/50; ISO 306 | |||
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |||
| Flame Spread | 2.00 mm/min @Thickness 3.00 mm |
0.0787 in/min @Thickness 0.118 in |
FMVSS Buring Speed | ||
| 6.00 mm/min @Thickness 2.00 mm |
0.236 in/min @Thickness 0.0787 in |
FMVSS Buring Speed | |||
| Oxygen Index | 27 % | 27 % | ISO 4589 | ||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Zone 1 | ||
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Zone 2 | ||
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Zone 3 | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | 0.20 % | 0.20 % | |||
| De |
|||||
| Potable Water | ACS WRAS | ||||
| UL f1 | f1 | ||||
1、具高抗张强度；2、耐韧、耐冲击性特优；3、自润性、耐磨性佳、耐药品性优；4、低温特性佳；5、具自熄性；