自润性、PA66 R1000HI620 冲击改性、_产品资讯

PA66 R1000HI620 塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。

颗粒样图：

Physical Properties	Metric	English	Comments
物性表：
Density	1.07 g/cc	0.0387 lb/in³	ISO 1183
Moisture Absorption	1.50 % @Temperature 23.0 °C	1.50 % @Temperature 73.4 °F	50% RH; ISO 62
Water Absorption at Saturation	5.5 % @Temperature 23.0 °C	5.5 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow	0.010 - 0.012 cm/cm	0.010 - 0.012 in/in	on Tensile Bar; E2P method

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	112	112	ISO 2039-2
Tensile Strength, Yield	50.0 MPa	7250 psi	50 mm/min; ISO 527
Elongation at Break	>= 100 %	>= 100 %	50 mm/min; ISO 527
Elongation at Yield	4.6 %	4.6 %	50 mm/min; ISO 527
Tensile Modulus	1.90 GPa	276 ksi	1 mm/min; ISO 527
Flexural Yield Strength	72.0 MPa	10400 psi	2 mm/min; ISO 178
Flexural Modulus	1.90 GPa	276 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	55.0 kJ/m² @Temperature -40.0 °C	26.2 ft-lb/in² @Temperature -40.0 °F	80x10x4; ISO 180/1A
	65.0 kJ/m² @Temperature -20.0 °C	30.9 ft-lb/in² @Temperature -4.00 °F	80x10x4; ISO 180/1A
	80.0 kJ/m² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	80x10x4; ISO 180/1A
Charpy Impact Unnotched	>= 10.0 J/cm² @Temperature 23.0 °C	>= 47.6 ft-lb/in² @Temperature 73.4 °F	Edgew 80x10x4 sp=62; ISO 179/1eU
	>= 10.0 J/cm² @Temperature -30.0 °C	>= 47.6 ft-lb/in² @Temperature -22.0 °F	Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched	6.50 J/cm² @Temperature -30.0 °C	30.9 ft-lb/in² @Temperature -22.0 °F	Edgew 80x10x4 sp=62; ISO 179/1eA
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	Edgew 80x10x4 sp=62; ISO 179/1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+16 ohm	>= 1.00e+16 ohm	IEC 60093
Dielectric Constant	2.7 @Frequency 1.00e+6 Hz	2.7 @Frequency 1.00e+6 Hz	IEC 60250
	2.9 @Frequency 50.0 - 60.0 Hz	2.9 @Frequency 50.0 - 60.0 Hz	IEC 60250
Dielectric Strength	16.0 kV/mm @Thickness 3.20 mm	406 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
Dissipation Factor	0.0067 @Frequency 50.0 - 60.0 Hz	0.0067 @Frequency 50.0 - 60.0 Hz	IEC 60250
	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	550 V	550 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 µm/m-°C @Temperature 23.0 - 60.0 °C	55.6 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	120 µm/m-°C @Temperature 23.0 - 60.0 °C	66.7 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	72.0 °C	162 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point	190 °C	374 °F	B/120; ISO 306
	192 °C	378 °F	B/50; ISO 306
UL RTI, Electrical	65.0 °C	149 °F
UL RTI, Mechanical with Impact	65.0 °C	149 °F
UL RTI, Mechanical without Impact	65.0 °C	149 °F
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in
Flame Spread	15.0 mm/min @Thickness 2.00 mm	0.591 in/min @Thickness 0.0787 in	FMVSS Burning Speed

Processing Properties	Metric	English	Comments
Zone 1	260 - 270 °C	500 - 518 °F
Zone 2	270 - 280 °C	518 - 536 °F
Zone 3	270 - 280 °C	518 - 536 °F
Melt Temperature	270 - 280 °C	518 - 536 °F
Mold Temperature	60.0 - 100 °C	140 - 212 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.20 %	0.20 %

应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。