颗粒样图：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec |
1.3 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.016 cm/cm @Thickness 3.20 mm |
0.0090 - 0.016 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm |
30 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 113 MPa @Thickness 6.40 mm |
16400 psi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 3.04 GPa @Thickness 6.40 mm |
441 ksi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 1.00 mm |
559 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 180 - 240 sec | 180 - 240 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | |
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness 0.750 - 0.820 mm |
15 - 30 sec @Thickness 0.0295 - 0.0323 in |
|
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 0.750 mm |
>= 120 arcs @Thickness 0.0295 in |
|
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 50.0 mm/min | 1.00 - 1.97 in/min | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C @Thickness 6.40 mm |
464 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| Flammability, UL94 | V-0 @Thickness >=0.800 mm |
V-0 @Thickness >=0.0315 in |
|
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 255 - 280 °C | 491 - 536 °F | Injection Molding |
| Middle Barrel Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Front Barrel Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |