物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183/A | ||
| Water Absorption | 0.75 % @Temperature 23.0 °C, Time 86400 sec |
0.75 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | ||
| Viscosity | 110 cP @Shear Rate 1000 1/s, Temperature 300 °C |
110 cP @Shear Rate 1000 1/s, Temperature 572 °F |
|||
| 200 cP @Shear Rate 1000 1/s, Temperature 280 °C |
200 cP @Shear Rate 1000 1/s, Temperature 536 °F |
||||
| 200 cP @Shear Rate 100 1/s, Temperature 300 °C |
200 cP @Shear Rate 100 1/s, Temperature 572 °F |
||||
| 300 cP @Shear Rate 100 1/s, Temperature 280 °C |
300 cP @Shear Rate 100 1/s, Temperature 536 °F |
||||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A | ||
| Tensile Stress | 30.0 MPa @Strain 0.500 % |
4350 psi @Strain 0.500 % |
|||
| 95.0 MPa @Strain 1.00 % |
13800 psi @Strain 1.00 % |
||||
| 130 MPa @Strain 1.50 % |
18900 psi @Strain 1.50 % |
||||
| 150 MPa @Strain 2.00 % |
21800 psi @Strain 2.00 % |
||||
| 170 MPa @Strain 2.50 % |
24700 psi @Strain 2.50 % |
||||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A | ||
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 | ||
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Comparative Tracking Index | 250 V | 250 V | Solution B; IEC 60112 | ||
| 300 V | 300 V | Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 5.40 µm/m-°C @Temperature 23.0 - 85.0 °C |
3.00 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 | ||
| Melting Point | 263 °C | 505 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75/Af | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
ISO 1210 | ||
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
ISO 1210 | |||
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
ISO 1210 | |||
| Oxygen Index | 30.5 % | 30.5 % | ISO 4589 | ||
| Glow Wire Test | 725 °C | 1340 °F | Ignition Temperature; ISO 60695-2-13 | ||
| 960 °C | 1760 °F | ISO 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 270 - 275 °C | 518 - 527 °F | |||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 275-280°C | ||||
| Fire and smoke F index | I3/F3 | NF F 16 101 | |||
| Mixing Zone | 280-285°C | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。