颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.0 - 6.0 % | 5.0 - 6.0 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted | ||
| Linear Mold Shrinkage, Flow | 0.0041 cm/cm | 0.0041 in/in | TM=320°C, TW=100°C | ||
| 0.0050 cm/cm | 0.0050 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 150 MPa | 21800 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 8.30 GPa | 1200 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | ||
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | ||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00 Hz |
4.0 @Frequency 1.00 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 | ||
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | for 50% loss of tensile strength after 20000hr | ||
| 150 °C | 302 °F | for 50% loss of tensile strength after 5000hr | |||
| 270 °C | 518 °F | ||||
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 350 °C | >= 662 °F | |||
| Flammability, UL94 | V-2 @Thickness >=0.370 mm |
V-2 @Thickness >=0.0146 in |
|||
| V-0 @Thickness >=0.750 mm |
V-0 @Thickness >=0.0295 in |
||||
| 5VB @Thickness >=1.50 mm |
5VB @Thickness >=0.0591 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 300 °C | 572 °F | Feed Zone | ||
| Zone 2 | 310 °C | 590 °F | Compression | ||
| Zone 3 | 320 °C | 608 °F | Metering-zone | ||
| Zone 4 | 320 °C | 608 °F | Nozzle | ||
| Melt Temperature | >= 320 °C | >= 608 °F | Optimal | ||
| 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding | ||
| 100 °C | 212 °F | Optimal | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 8 hour | 8 hour | |||
| De |
|||||
| Color | BK 00100 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >470°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。