| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.9 - 6.5 % | 5.9 - 6.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.8 - 2.2 % | 1.8 - 2.2 % | ISO 62 | ||
| >= 2.0 % | >= 2.0 % | 50% RH | |||
| >= 6.2 % | >= 6.2 % | Saturation | |||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | |||
| Melt Flow | 63.45 g/10 min @Load 5.00 kg, Temperature 275 °C |
63.45 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 280 MPa | 40600 psi | ISO 178 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 19.0 kJ/m² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | ||
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.021 @Frequency 1.00e+6 Hz |
0.021 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 575 V | 575 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 - 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
8.33 - 11.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 60.0 - 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
33.3 - 38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 | ||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612-1 | ||
| Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feed Zone | ||
| Zone 2 | 370 °C | 698 °F | Compression | ||
| Zone 3 | 280 °C | 536 °F | Metering-zone | ||
| Zone 4 | 280 °C | 536 °F | Nozzle | ||
| Melt Temperature | 280 °C | 536 °F | Optimal | ||
| 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| De |
|||||
| Color | BK 00564 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。