PA6 B3WG3 15%玻璃、_产品资讯

PA6 B3WG3 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Mechanical Properties	Metric	English	Comments

Flexural Modulus	5.40 GPa	783 ksi	ISO 178
Izod Impact, Notched (ISO)	5.60 kJ/m²	2.66 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ISO 3146
UL RTI, Electrical	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	746B
UL RTI, Mechanical with Impact	85.0 °C @Thickness 1.50 mm	185 °F @Thickness 0.0591 in	746B
UL RTI, Mechanical without Impact	130 °C @Thickness 1.50 mm	266 °F @Thickness 0.0591 in	746B
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 290 °C	482 - 554 °F
Mold Temperature	80.0 - 95.0 °C	176 - 203 °F
Dry Time	2 - 4 hour	2 - 4 hour

Descriptive Properties
Commercial Status	North America

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。